Semiconductor component having through-silicon vias

ABSTRACT

A semiconductor component includes a substrate having an opening. The semiconductor component further includes a first dielectric liner in the opening, wherein the first dielectric liner having a thickness T1 at a first end of the opening, and a thickness T2 at a second end of the opening, and R1 is a ratio of T1 to T2. The semiconductor component further includes a second dielectric liner over the first dielectric liner, wherein the second dielectric liner having a thickness T3 at the first end of the opening, a thickness T4 at the second end of the opening, R2 is a ratio of T3 to T4, and R1 is greater than R2.

PRIORITY CLAIM

This application is a continuation of U.S. application Ser. No.16/168,306, filed Oct. 23, 2018, which is a continuation of U.S.application Ser. No. 15/214,776, filed Jul. 20, 2016, now U.S. Pat. No.10,115,634, issued Oct. 30, 2018, which is a divisional of U.S.application Ser. No. 14/033,862, filed Sep. 23, 2013, now U.S. Pat. No.9,418,923, issued Aug. 16, 2016, which is continuation of U.S.application Ser. No. 13/799,760, filed Mar. 13, 2013, now U.S. Pat. No.8,575,725, issued Nov. 5, 2013, which is a divisional of U.S.application Ser. No. 13/085,668, filed Apr. 13, 2011, now U.S. Pat. No.8,487,410, issued Jul. 16, 2013, which are incorporated herein byreference in their entireties.

TECHNICAL FILED

The disclosure relates generally to a semiconductor device, and moreparticularly to a structure and method for forming through-silicon vias.

BACKGROUND

Since the invention of integrated circuits, the semiconductor industryhas experienced continuous rapid growth due to constant improvements inthe integration density of various electronic components (i.e.,transistors, diodes, resistors, capacitors, etc.). For the most part,this improvement in integration density has come from repeatedreductions in minimum feature size, allowing more components to beintegrated into a given chip area.

These integration improvements are essentially two-dimensional (2D) innature, in that the volume occupied by the integrated components isessentially on the surface of the semiconductor wafer. Although dramaticimprovements in lithography have resulted in considerable improvementsin 2D integrated circuit formation, there are physical limitations tothe density that can be achieved in two dimensions. One of theselimitations is the minimum size needed to make these components. Also,when more devices are put into one chip, more complex designs arerequired.

An additional limitation comes from the significant increase in thenumber and lengths of interconnections between devices as the number ofdevices increases. When the number and the lengths of interconnectionsincrease, both circuit RC delay and power consumption increase.

Among the efforts for resolving the above-discussed limitations,three-dimensional integrated circuit (3D IC) and stacked dies arecommonly used. Through-silicon vias (TSVs) are thus used in 3D IC andstacked dies for connecting dies. In this case, TSVs are often used toconnect the integrated circuits on a die to the backside of the die. Inaddition, TSVs are also used to provide short grounding paths forgrounding the integrated circuits through the backside of the die, whichmay be covered by a grounded metallic film.

The formation of the TSVs requires more process steps. The integratedcircuit formation thus becomes more complicated, and hence problems mayoccur. New methods for forming TSVs are thus needed to continuouslyimprove the TSV formation process.

BRIEF DESCRIPTION OF THE DRAWINGS

Aspects of the present disclosure are best understood from the followingdetailed description when read with the accompanying figures. It isemphasized that, in accordance with the standard practice in theindustry, various features are not drawn to scale. In fact, thedimensions of the various features may be arbitrarily increased orreduced for clarity of discussion.

FIG. 1 is a flowchart of a method for fabricating through-silicon viasaccording to embodiments of the disclosure.

FIGS. 2 to 9 are cross-sectional views for forming through-silicon viasat various stages of manufacture according to FIG. 1 .

DETAILED DESCRIPTION

It is to be understood that the following disclosure provides manydifferent embodiments, or examples, for implementing different featuresof the disclosure. Specific examples of components and arrangements aredescribed below to simplify the present disclosure. These are, ofcourse, merely examples and are not intended to be limiting. Moreover,the formation of a first feature over, above, or on a second feature inthe description that follows may include embodiments in which the firstand second features are formed in direct contact, and may also includeembodiments in which additional features may be formed interposing thefirst and second features, such that the first and second features maynot be in direct contact. Various features may be arbitrarily drawn indifferent scales for simplicity and clarity.

Illustrated in FIG. 1 is a flowchart of a method 11 for fabricating asemiconductor component with through-silicon vias according toembodiments of the disclosure. FIG. 2 to FIG. 9 are cross-sectionalviews showing various stages during fabrication of a semiconductorcomponent 100 with through-silicon vias according to one or moreembodiments according to FIG. 1 . It is noted that some processes mayonly be briefly described herein for the sake of simplicity and clarity.Accordingly, it is understood that additional processes may be providedbefore, during, and after the method 11 of FIG. 1 .

Referring now to FIG. 1 , method 11 for fabricating a semiconductorcomponent with through-silicon vias begins with operation 13. Atoperation 13, a semiconductor substrate is provided. A plurality of diesis fabricated on a semiconductor substrate. The dies on thesemiconductor substrate are divided by scribe lines between the dies.The term “semiconductor substrate” herein generally refers to thesemiconductor bulk substrate on which various layers and devicestructures may or may not be formed. In some embodiments, thesemiconductor bulk substrate includes silicon or a compoundsemiconductor, such as GaAs, InP, Si/Ge, or SiC. Examples of such layersinclude dielectric layers, doped layers, polysilicon layers orconductive layers. Examples of device structures include transistors,resistors, and/or capacitors, which may or may not be interconnectedthrough an interconnect layer to additional active circuits.

Next, method 11 continues with operation 15 in which the semiconductorsubstrate is patterned to form an opening in the semiconductorsubstrate.

Referring to FIG. 2 , a magnified view of a portion of the semiconductorcomponent 100 with a semiconductor substrate 101 is provided. Thesemiconductor substrate 101 having a top surface 102. A plurality ofopenings 103 are formed, extending through the top surface 102 into apredetermined depth of semiconductor substrate 101. In this example,only one opening 103 is shown for illustration purposes. In at least oneembodiment, the opening 103 comprises a depth in a range of about 5 μmto about 150 μm, and a width in a range of about 1 μm to about 20 μm.The opening 103 comprises an interior surface 105, which is consisted ofsidewalls, and a bottom surface 106 of the opening 103. The opening 103further comprises a top portion 107 and a bottom portion 109. The topportion 107 is adjacent to the topmost of the opening 103 and also closeto the top surface 102 of the semiconductor substrate 101. The bottomportion 109 is adjacent to the bottommost of the opening 103 and alsoclose to the bottom surface 106 of the opening 103.

In one embodiment, the opening 103 may be formed by a dry etchingprocess. Alternatively, the opening 103 may be formed by laser drilling.In one embodiment, a patterned masking layer (not shown) is formed overthe semiconductor substrate 101 to cover the un-removed areas and exposeportions of the semiconductor substrate 101 to enable the formation ofthe opening 103. The masking layer may be a hardmask comprising siliconnitride, oxide, or oxynitride formed through a process such as chemicalvapor deposition (CVD). Once formed, the masking layer is patternedthrough suitable photolithographic and etching processes to expose thoseportions of the semiconductor substrate 101 that will form the opening103. Then, the exposed semiconductor substrate 101 is removed by etchingor laser drilling to form the opening 103. In another embodiment, apatterned and developed photoresist, may alternatively be utilized toprotect the un-removed areas of the semiconductor substrate 101 whileexposing portions of the substrate 101 to be removed to form the opening103.

Referring back to FIG. 1 , method 11 continues with operation 17 inwhich a first dielectric liner is deposited by a plasma enhancedchemical vapor deposition (PECVD) on the interior surface of theopening.

FIG. 3 illustrates the stage of operation 17 in which a cross-sectionalview of the semiconductor component 100 is provided. A first dielectricliner 111 is formed on the interior surface 105 of the opening 103. Thefirst dielectric liner 111 has a thickness T₁ on the top portion 107 ofthe opening 103 and a thickness T₂ on the bottom portion 109 of theopening 103. The thickness T₁ is in a range of about 200 Å to about 2000Å, and the thickness T₂ is in a range of about 20 Å to about 200 Å. Thefirst dielectric liner 111 becomes thinner gradually from the topportion 107 to the bottom portion 109. A ratio R₁ of the thickness T₁ tothe thickness T₂ is about 5 to about 20. The first dielectric liner 111may include silicon oxide, silicon nitride, silicon oxynitride, or PSG.

In one embodiment, the first dielectric liner 111 is formed by PECVD. Inthis example, a silicon oxide layer is formed as the first dielectricliner in a plasma environment comprising O₃ and TEOS. The flow rates ofO₃ and TEOS are in a range of about 5000 standard cubic centimeters perminute (sccm) to about 10000 sccm, and of about 500 milligram per minute(mgm) to about 3000 mgm, respectively. An operation power of the plasmaenvironment uses high frequency RF power set at about 300 W to about 500W at 13.56 MHz, and low frequency RF power set at about 50 W to about150 W at 350 kHz. An operation pressure of the plasma environment isabout 2 Torr to about 8 Torr. An operation temperature on the substrate101 of the semiconductor component 100 is about 150° C. to about 450° C.Under the above described conditions, the first dielectric liner 111 isformed with a first compressive stress within a range of about 100 MPato about 400 MPa. The first dielectric liner 111 has a first etchingrate of about 1 Å/min to about 10 Å/min in a HF solution, which isdiluted at a rate of 1000:1. This disclosure is not limited to the aboveconditions for forming first dielectric liner 111, and differingconditions that produce either the above compressive stress or the aboveetch rate are within the scope of this disclosure.

PECVD uses a radio frequency (RF) power to generate a glow discharge totransfer the energy into the reactant gases, allowing the deposition onthe interior surface 105 of the opening 103 and the top surface 102 ofthe semiconductor substrate 101 at a lower temperature. It is believedthat the radicals with high energy in the plasma of PECVD repair thedamaged interior surface 105 during operation 15 for the opening 103formation. The dangling bonds and the defects on the interior surface105 are removed. The interface between the first dielectric liner 111and the interior surface 105 has fewer defects than conventionalmethods. Thus, desirable properties such as good adhesion, low pinholedensity and adequate electrical properties of the deposited firstdielectric liner 111 are produced.

Referring back to FIG. 1 , method 11 continues with operation 19 inwhich a second dielectric liner is deposited by a conformal depositionon the first dielectric liner.

FIG. 4 illustrates the stage of operation 19 in which a seconddielectric liner 113 is formed on the first dielectric liner 111. Thesecond dielectric liner 113 has a thickness T₃ on the top portion 107 ofthe opening 103 and a thickness T₄ on the bottom portion 109 of theopening 103. The thickness T₃ is in a range of about 500 Å to about 2500Å, and the thickness T₄ is in a range of about 500 Å to about 2500 Å. Inone embodiment, the second dielectric liner 113 may be a completelyconformal liner, some variation in the conformality of the second linerthickness has been found to have beneficial effects. A ratio R₂ of thethickness T₃ to the thickness T₄ is about 1 to about 5. Within the rangeof the ratio R₂, the second dielectric liner 113 still maintainsbeneficial effects of conformality.

In one embodiment, the second dielectric liner 113 is formed by highaspect ratio process (HARP) using an O₃/TEOS based sub atmosphericchemical vapor deposition process. In this example, an oxide layer isformed as the second dielectric liner. The flow rates of O₃ and TEOS arebe in a range of about 10000 standard cubic centimeters per minute(sccm) to about 20000 sccm, and of about 500 mgm to about 3500 mgm,respectively. An operation pressure is about 400 Torr to about 650 Torr.An operation temperature on the semiconductor component 100 is about200° C. to about 450° C. The reactants are heated under the operationtemperature without plasma and deposit on the first dielectric liner111. Under the above described condition, the second dielectric liner113 is formed with a tensile stress within a range of about 50 MPa toabout 300 MPa. The second dielectric liner 113 has a second etching rateof about 10 Å/min to about 50 Å/min in a HF solution, which is dilutedat a rate of 1000:1. Alternatively, the second dielectric liner 113 maybe formed by using a conformal deposition technique, such as atomiclayer deposition (ALD) or a spin on dielectric (SOD) such as a silicate,a siloxane, a methyl SilsesQuioxane (MSQ), a hydrogen SisesQuioxane(HSQ), an MSQ/HSQ, a perhydrosilazane (TCPS) or a perhydro-polysilazane(PSZ).

This disclosure is not limited to the above conditions for forming thesecond dielectric liner 113, and different conditions that produceeither the above compressive stress or the above etch rate are withinthe scope of this disclosure.

According to the above description, the ratio R₁ is greater than theratio R₂. The second dielectric liner 113 has better conformality thanthe first dielectric liner 111. The second dielectric liner 113 smoothsover the variation of the thickness of the combined layer of liner 111and liner 113. The first etching rate is less than the second etchingrate. Hence, the first dielectric liner 111 has a lower pinhole densitythan the second dielectric liner 113. The first dielectric liner 111provides protection from moisture or contaminations diffuse from thesemiconductor substrate 101 into the second dielectric liner 113.

Referring back to FIG. 1 , method 11 continues with operation 21 inwhich a third dielectric liner is deposited by a plasma enhancedchemical vapor deposition (PECVD) on the second dielectric liner.

FIG. 5 illustrates the stage of operation 21 in which a cross-sectionalview of the semiconductor component 100 is provided. A third dielectricliner 115 is formed on the second dielectric liner 113. The thirddielectric liner 115 has a thickness T₅ on the top portion 107 of theopening 103 and a thickness T₆ on the bottom portion 109 of the opening103. The thickness T₅ is in a range of about 200 Å to about 2000 Å, andthe thickness T₆ is in a range of about 20 Å to about 200 Å. The thirddielectric liner 115 becomes thinner gradually from the top portion 107to the bottom portion 109. A ratio R₃ of the thickness T₅ to thethickness T₆ is about 5 to about 20. The third dielectric liner 115 mayinclude silicon oxide, silicon nitride, silicon oxynitride, or PSG.

In one embodiment, the third dielectric liner 115 is formed by PECVD. Inthis example, a silicon oxide layer is formed as the third dielectricliner in a plasma environment comprising O₃ and TEOS. The flow rates ofO₃ and TEOS are in a range of about 5000 standard cubic centimeters perminute (sccm) to about 10000 sccm, and of about 500 mgm to about 3000mgm, respectively. An operation power of the plasma environment useshigh frequency RF power set at about 300 W to about 500 W at 13.56 MHz,and low frequency RF power set at about 50 W to about 150 W at 350 kHz.An operation pressure of the plasma environment is about 2 Torr to about8 Torr. An operation temperature on the semiconductor component 100 isabout 150° C. to about 450° C. Under the above described condition, thethird dielectric liner 115 is formed with a second compressive stresswithin a range of about 100 MPa to about 400 MPa. The third dielectricliner 115 has a third etching rate of about 1 Å/min to about 10 Å/min ina HF solution, which is diluted at a rate of 1000:1.

This disclosure is not limited to the above conditions for the formationof third dielectric liner 115, and other conditions that produce eitherthe above compressive stress or the above etch rate are within the scopeof this disclosure.

In one embodiment, the first dielectric liner 111 and the thirddielectric liner 115 comprise the same dielectric material. The firstcompressive stress of the first dielectric liner 111 and the secondcompressive stress of the third dielectric liner 115 are equal. Inanother embodiment, the first dielectric liner 111 and the thirddielectric liner 115 comprise different dielectric materials. The firstcompressive stress of the first dielectric liner 111 and the secondcompressive stress of the third dielectric liner 115 are different. Atleast one of the first compressive stress and the second compressivestress is within a range of about 100 MPa to about 400 MPa.

According to the above description, the third etching rate is less thanthe second etching rate. The third dielectric liner 115 may have a lowerpinhole density than the second dielectric liner 113. The thirddielectric liner 115 is formed between the second dielectric liner 113and the later formed metal barrier layer 117 (shown in FIG. 6 ). Thethird dielectric liner 115 provides protection from contaminationsdiffuse from the later formed metal barrier layer 117 and the conductivematerial 119 into the semiconductor substrate 101. A robust electricalperformance of the semiconductor component 100 is provided.

Referring back to FIG. 1 , method 11 continues with operation 23 inwhich a metal barrier layer is deposited on the third dielectric liner.

FIG. 6 illustrates the stage of operation 23 in which a cross-sectionalview of the semiconductor component 100 is provided. A metal batherlayer 117 is formed on the third dielectric liner 115. The metal barrierlayer 117 may provide protection from metal ions, contaminations diffusefrom the later formed conductive material 119 into the semiconductorsubstrate 101. The metal barrier layer 117 comprises tantalum nitride,although other materials, such as tantalum, titanium, titanium nitride,combinations of these, may alternatively be used. The formation methodsof the metal barrier layer 117 include ALD, PECVD, or physical vapordeposition (PVD) processes.

Referring back to FIG. 1 , method 11 continues with operation 25 inwhich the remaining opening after the deposition of the three dielectricliners and the metal barrier layer is filled with a conductive material.

Referring to FIG. 7 , the remaining opening 103 after the deposition ofthe three dielectric liners and the metal barrier layer 117 is filledwith a conductive material 119. The conductive material 119 may overfillthe remaining opening 103 and the metal barrier layer 117. Theconductive material 119 may include copper or copper alloys. However,other metals, such as aluminum, silver, gold, and combinations thereof,may also be used. The possible formation methods include electrolessplating, or other commonly used deposition methods such as sputtering,printing, electro plating, and chemical vapor deposition (CVD).

Referring back to FIG. 1 , method 11 continues with operation 27 inwhich the excess conductive material 119, the metal barrier layer 117and the three dielectric liners outside of the opening 103 is optionallyremoved.

FIG. 8 illustrates the stage of operation 27 in which a cross-sectionalview of the semiconductor component 100 is provided. The excessmaterials outside of the opening 103 are removed through a suitableprocess such as chemical mechanical polishing (CMP), an etching, or acombination of polishing and etching. The removal process preferablyremoves any conductive material 119 that is located over the metalbarrier layer 117 and the three dielectric liners 111, 113 and 115 aswell, so that the removal of excess materials will expose the topsurface 102 of the semiconductor substrate 101 for further processsteps. A through-silicon via 120 with the conductive material 119 filledin the opening 103 is formed.

In some embodiments, further process steps are optionally followed afterthe operation 27. Metallization layers (not shown) may be formed overthe top surface 102 of the substrate 101 and are designed to connect thedevice structures (not shown) in the semiconductor component 100 to formfunctional circuitry and also to form a connection to the opposite sideof the substrate 101 through the TSV 120. The metallization layers maybe formed of alternating layers of dielectric and conductive materialand may be formed through any suitable process (such as deposition, dualdamascene).

Referring back to FIG. 1 , method 11 continues with operation 29 inwhich a thinning process performed over the backside of the substrate toexpose the TSV.

FIG. 9 illustrates the stage of operation 29 in which a cross-sectionalview of the semiconductor component 100 is provided. A portion of thebackside of the semiconductor substrate 101 is then removed to exposethe conductive material 119 located within the opening 103 to completethe TSV 120. The removal may be performed with a grinding process suchas a chemical mechanical polish (CMP), although other suitableprocesses, such as etching, may alternatively be used. The removal ofthe backside of the substrate 101 may be continued until the substrate101 has a thickness of between about 10 μm and about 200 μm. Thereafter,the TSV 120 is exposed from backside of the substrate 101. Thethrough-silicon via (TSV) 120 provides electrical connection for thesemiconductor component formed on substrate 101 to other components.

Various embodiments of the present invention may be used to improve theconventional through-silicon via structures. For example, in the variousembodiments the first dielectric liner 111 formed by PECVD repairs thedamaged interior surface 105 of the opening 103. The first dielectricliner 111 provides protection from contaminations diffuse from thesubstrate 101 into the second dielectric liner 113 and inner layers 115,117 and 119. The second dielectric liner 113 with conformal thicknesssmoothes over the variation of the thickness of the combined layer ofliners 111, 113 and 115. The compressive stresses of the firstdielectric liner and the third dielectric liner in combination with thetensile stress in the second dielectric liner adjust the overall stressin the TSV 120. The leakage current, device performance and yield on thecompleted products are thus significantly increased.

Although, the semiconductor component having through-silicon vias andthe method of making the same are described according variousembodiments of the present disclosure, other alternatives, replacementsor modifications may present without departure from the spirit of thepresent disclosure.

An embodiment of the disclosure provides a semiconductor component. Thesemiconductor component includes a semiconductor substrate having anopening. A first dielectric liner having a first compressive stress isdisposed in the opening. A second dielectric liner having a tensilestress is disposed on the first dielectric liner. A third dielectricliner having a second compressive stress disposed on the seconddielectric liner.

The present disclosure also provides another embodiment of asemiconductor component. The semiconductor component includes asubstrate having a top surface. The semiconductor component furtherincludes an opening. The semiconductor component further includes afirst dielectric liner having a first stress disposed in the opening.The semiconductor component further includes a second dielectric linerhaving a second stress disposed on the first dielectric liner, wherein adirection of the first stress is opposite a direction of the secondstress. The semiconductor component further includes a third dielectricliner having a third stress disposed on the second dielectric liner,wherein a direction of the third stress is equal to the direction of thefirst stress. The semiconductor component further includes a conductivematerial disposed on within the third dielectric liner.

The present disclosure also provides another embodiment of a method offorming a semiconductor component. The method includes forming anopening in a semiconductor substrate. A first dielectric liner isdeposited on the interior surface by a plasma enhanced chemical vapordeposition (PECVD). A second dielectric liner is deposited on the firstdielectric liner by a conformal deposition. A third dielectric liner isdeposited on the second dielectric liner by a PECVD.

An aspect of this description relates to a semiconductor component. Thesemiconductor component includes a substrate having an opening. Thesemiconductor component further includes a first dielectric liner in theopening, wherein the first dielectric liner having a thickness T₁ at afirst end of the opening, and a thickness T₂ at a second end of theopening, and R₁ is a ratio of T₁ to T₂. The semiconductor componentfurther includes a second dielectric liner over the first dielectricliner, wherein the second dielectric liner having a thickness T₃ at thefirst end of the opening, a thickness T₄ at the second end of theopening, R₂ is a ratio of T₃ to T₁, and R₁ is greater than R₂. In someembodiments, the opening extends through an entirety of the substrate.In some embodiments, the semiconductor component further includes aconductive material surrounded by the second dielectric liner. In someembodiments, the ratio R₁ ranges from about 5 to about 20. In someembodiments, the ratio R₂ ranges from about 1 to about 5. In someembodiments, the second dielectric liner comprises an oxide layer. Insome embodiments, the first dielectric liner has an etching rate ofabout 1 angstrom/minute (A/min) to about 10 Å/min in a HF solution.

An aspect of this description relates to a semiconductor component. Thesemiconductor component includes a substrate having an opening. Thesemiconductor component further includes a first dielectric liner in theopening, wherein the first dielectric liner having a thickness T₁ at afirst end of the opening, and a thickness T₂ at a second end of theopening, and R₁ is a ratio of T₁ to T₂. The semiconductor componentfurther includes a second dielectric liner over the first dielectricliner, wherein the second dielectric liner having a thickness T₃ at thefirst end of the opening, a thickness T₄ at the second end of theopening, R₂ is a ratio of T₃ to T₁, and R₁ is less than R₂. In someembodiments, the ratio R₁ ranges from about 1 to about 5. In someembodiments, the ratio R₂ ranges from about 5 to about 20. In someembodiments, the semiconductor component further includes a thirddielectric liner in the opening, wherein the third dielectric linerhaving a thickness T₅ at the first end of the opening, and a thicknessT₆ at the second end of the opening, and R₃ is a ratio of T₅ to T₆. Insome embodiments, R₃ is greater than R₁. In some embodiments, R₃ isequal to R₂. In some embodiments, the third dielectric liner is betweenthe substrate and the first dielectric liner. In some embodiments, thefirst dielectric liner is between the second dielectric liner and thethird dielectric liner. In some embodiments, the semiconductor componentfurther includes a conductive material surrounded by the seconddielectric liner.

An aspect of this description relates to a semiconductor component. Thesemiconductor component includes a substrate having an opening. Thesemiconductor component further includes a first dielectric liner in theopening, wherein the first dielectric liner having a thickness T₁ at afirst end of the opening, and a thickness T₂ at a second end of theopening, and R₁ is a ratio of T₁ to T₂. The semiconductor componentfurther includes a second dielectric liner over the first dielectricliner, wherein the second dielectric liner having a thickness T₃ at thefirst end of the opening, a thickness T₄ at the second end of theopening, R₂ is a ratio of T₃ to T₄, and R₁ is equal to R₂. In someembodiments, the ratio R₁ ranges from about 5 to about 20. In someembodiments, the semiconductor component further includes a thirddielectric liner between the first dielectric liner and the seconddielectric liner. In some embodiments, the semiconductor componentfurther includes a conductive material surrounded by the seconddielectric liner.

Although the embodiments and its advantages have been described indetail, it should be understood that various changes, substitutions andalterations can be made herein without departing from the spirit andscope of the invention as defined by the appended claims. Moreover, thescope of the present application is not intended to be limited to theparticular embodiments of the process, machine, manufacture, andcomposition of matter, means, methods and steps described in thespecification. As one of ordinary skill in the art will readilyappreciate from the disclosure of the present invention, processes,machines, manufacture, compositions of matter, means, methods, or steps,presently existing or later to be developed, that perform substantiallythe same function or achieve substantially the same result as thecorresponding embodiments described herein may be utilized according tothe present invention. Accordingly, the appended claims are intended toinclude within their scope such processes, machines, manufacture,compositions of matter, means, methods, or steps.

What is claimed:
 1. A semiconductor component comprising: a substratehaving an opening; a first dielectric liner in the opening, wherein thefirst dielectric liner having a thickness T₁ at a first end of theopening, and a thickness T₂ at a second end of the opening, and R₁ is aratio of T₁ to T₂, and a second dielectric liner over the firstdielectric liner, wherein the second dielectric liner having a thicknessT₃ at the first end of the opening, a thickness T₄ at the second end ofthe opening, R₂ is a ratio of T₃ to T₄, and R₁ is greater than R₂. 2.The semiconductor component of claim 1, wherein the opening extendsthrough an entirety of the substrate.
 3. The semiconductor component ofclaim 1, further comprising a conductive material surrounded by thesecond dielectric liner.
 4. The semiconductor component of claim 1,wherein the ratio R₁ ranges from about 5 to about
 20. 5. Thesemiconductor component of claim 1, wherein the ratio R₂ ranges fromabout 1 to about
 5. 6. The semiconductor component of claim 1, whereinthe second dielectric liner comprises an oxide layer.
 7. Thesemiconductor component of claim 1, wherein the first dielectric linerhas an etching rate of about 1 angstrom/minute (A/min) to about 10 A/minin a HF solution.
 8. A semiconductor component comprising: a substratehaving an opening; a first dielectric liner in the opening, wherein thefirst dielectric liner having a thickness T₁ at a first end of theopening, and a thickness T₂ at a second end of the opening, and R₁ is aratio of T₁ to T₂, and a second dielectric liner over the firstdielectric liner, wherein the second dielectric liner having a thicknessT₃ at the first end of the opening, a thickness T₄ at the second end ofthe opening, R₂ is a ratio of T₃ to T₄, and R₁ is different from R₂. 9.The semiconductor component of claim 8, wherein the ratio R₁ ranges fromabout 1 to about
 5. 10. The semiconductor component of claim 8, whereinthe ratio R₂ ranges from about 5 to about
 20. 11. The semiconductorcomponent of claim 8, further comprising a third dielectric liner in theopening, wherein the third dielectric liner having a thickness T₅ at thefirst end of the opening, and a thickness T₆ at the second end of theopening, and R₃ is a ratio of T₅ to T₆.
 12. The semiconductor componentof claim 11, wherein R₃ is greater than R₁.
 13. The semiconductorcomponent of claim 11, wherein R₃ is equal to R₂.
 14. The semiconductorcomponent of claim 11, wherein the third dielectric liner is between thesubstrate and the first dielectric liner.
 15. The semiconductorcomponent of claim 11, wherein the first dielectric liner is between thesecond dielectric liner and the third dielectric liner.
 16. Thesemiconductor component of claim 8, further comprising a conductivematerial surrounded by the second dielectric liner.
 17. A semiconductorcomponent comprising: a substrate having an opening; a first dielectricliner in the opening, wherein the first dielectric liner having athickness T₁ at a first end of the opening, and a thickness T₂ at asecond end of the opening, and R₁ is a ratio of T₁ to T₂, and a seconddielectric liner over the first dielectric liner, wherein the seconddielectric liner having a thickness T₃ at the first end of the opening,a thickness T₄ at the second end of the opening, R₂ is a ratio of T₃ toT₄, R₁ is greater than R₂, and the second dielectric liner is entirelywithin the opening.
 18. The semiconductor component of claim 17, whereinthe ratio R₁ ranges from about 5 to about
 20. 19. The semiconductorcomponent of claim 17, further comprising a third dielectric linerbetween the first dielectric liner and the second dielectric liner. 20.The semiconductor component of claim 17, further comprising a conductivematerial surrounded by the second dielectric liner.